S-Plastic Stat-kon KEL22A a compound based on Acetal Homopolymer resin containing Carbon Fiber, PTFE. Added features include

Product Categories

Valox Plastic [1]
Ultem PEI Resin [197]
Cycoloy PC ABS [9]
Xenoy Resin [2]
Cycolac ABS [173]
Geloy Resin [110]
Colorcomp [20]
LNP Faradex [37]
S-Plastic Lubricomp [506]
LNP Stat Kon [308]
S-Plastic Thermocomp [705]
Plastic Resin Pellets Bulk [113]
Verton Plastic [106]

SAMTION INTERNATIONAL LIMITED

Contact Now

S-Plastic Stat-kon KEL22A a compound based on Acetal Homopolymer resin containing Carbon Fiber, PTFE. Added features include

Name: SPlastic Statkon KEL22A a compound based on Acetal Homopolymer resin containing Carbon Fiber PTFE Added features include
Brand: S-Plastic Stat-kon
Price: 1 USD

China S-Plastic Stat-kon KEL22A a compound based on Acetal Homopolymer resin containing Carbon Fiber, PTFE. Added features include wholesale

Brand Name : S-Plastic Stat-kon

Model Number : KEL22A

Certification : COA/ICP Test/Rohs/MSDS

Place of Origin : ——

MOQ : 100KG

Price : *USD

Payment Terms : L/C, T/T, Western Union, MoneyGram

Supply Ability : To be negotiated

Delivery Time : To be negotiated

Packaging Details : 25KG/bag

Melt Volume Rate, MVR at 260°C/2.16 kg : ？？？

UL Recognized, 94HB Flame Class Rating (3) : ？？？

Contact Now

S-Plastics Stat-kon KEL22A resin is a compound based on Acetal Homopolymer resin containing Carbon Fiber, PTFE. Added features
include: Electrically Conductive, Internally Lubricated.

Property

TYPICAL PROPERTIES (1)
MECHANICAL	Value	Unit	Standard
Tensile Stress, yield, 5 mm/min	56	MPa	ISO 527
Tensile Strain, yield, 5 mm/min	1	%	ISO 527
Tensile Modulus, 1 mm/min	8400	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	89	MPa	ISO 178
Flexural Stress, break, 2 mm/min	82	MPa	ISO 178
Flexural Strain, break, 2 mm/min	7.9	%	ISO 178
Flexural Modulus, 2 mm/min	6100	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, unnotched 80104 +23°C	20	kJ/m²	ISO 180/1U
Izod Impact, notched 80104 +23°C	5	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
CTE, 23°C to 60°C, flow	2.E-05	1/°C	ISO 11359-2
CTE, 23°C to 60°C, xflow	1.19E-04	1/°C	ISO 11359-2
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	135	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Mold Shrinkage, flow	0.33	%	S-Plastics Method
Density	1.48	g/cm³	ISO 1183
Water Absorption, 23°C/24hrs	0.5	%	ISO 62-1
ELECTRICAL	Value	Unit	Standard
Surface Resistivity	1.E+02 - 1.E+03	Ohm	ASTM D 257
Source GMD, last updated:07/15/2008

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	80	°C
Drying Time	4	hrs
Melt Temperature	200 - 215	°C
Front - Zone 3 Temperature	210 - 220	°C
Middle - Zone 2 Temperature	195 - 205	°C
Rear - Zone 1 Temperature	175 - 190	°C
Mold Temperature	80 - 110	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm
Source GMD, last updated:07/15/2008

Other related products we recommend:

For more information please download the datesheet
	S-Plastics Stat-kon KEL22A.pdf

Get The Latest Quotation

First-level distribution source in South China
Reduce procurement costs, improve supply stability,
Help you find the most suitable engineering plastic materials

Click to consult and get the latest quotation within 24 hours!